ליציקת חול מצופה היסטוריה ארוכה בתחום היציקה ומייצרת מספר רב של חלקי יציקה; אוּלָם, when producing precision חלקי פלדה יצוקים using castable sand casting, many problems arise: sticking (scabbing), cold separation, and air holes. How to solve these problems remains to be further explored.

אֲנִי. Understanding and knowledge of castable sand (castable sand belongs to the organic binder type and core sand)

1.1 Characteristics of castable sand: It has suitable strength performance; נזילות טובה, resulting in clear contours of the sand mold and core, dense structure, capable of manufacturing complex cores; the surface quality of the sand mold (ליבה) is good, with surface roughness reaching Ra = 6.3 – 12.5 מיקרומטר, dimensional accuracy reaching CT7 – CT9 grade; יכולת קריסה טובה, and the castings are easy to clean.

1.2 Application scope: Castable sand can be used to make both molds and cores; the mold or core made of castable sand can be used either in combination or in conjunction with other molds (cores); it can be used not only for gravity casting or low-pressure casting of metals, but also for iron mold castable sand casting, and for hot centrifugal casting; it can be used not only for the production of cast iron and non-ferrous alloy castings, but also for the production of cast steel parts.

II. Preparation of castable sand

2.1. Castable sand is generally composed of refractory materials, קלסרים, curing agents, lubricants, and special additives.

(1) Refractory materials are the main component of castable sand. The requirements for refractory materials are: high refractoriness, low volatiles, relatively round particles, and solid. בְּדֶרֶך כְּלַל, natural washed silica sand is selected. The requirements for silica sand are: high SiO2 content (for cast iron and non-ferrous alloy castings, it should be greater than 90%, for cast steel parts, it should be greater than 97%); the clay content should not exceed 0.3% (it is washed sand); [the clay content of water-washed sand is stipulated to be less than; the particle size 1: is distributed among 3 – 5 sieve sizes; the particle shape is round, the angular factor should not be greater than 1.3; the acid consumption value is not less than 5 ml.] (2) Binders are generally phenolic resin.

(3) Curing agents are usually urotropine; lubricants are generally calcium stearate, which functions to prevent the castable sand from caking and increase fluidity. The main role of additives is to improve the performance of castable sand.

(4) Basic composition and ratio of castable sand: Component Ratio (mass fraction, %) Explanation: Raw sand 100 Washed sand, phenolic resin 1.0 – 3.0 accounting for the weight of raw sand, urotropine (2% aqueous solution) 10 – 15 accounting for the weight of resin, calcium stearate 5 – 7 accounting for the weight of resin, תוספים 0.1 – 0.5 accounting for the weight of raw sand. 1: 2) 10 – 15 accounting for the weight of resin, calcium stearate 5 – 7 accounting for the weight of resin, תוספים 0.1 – 0.5 accounting for the weight of raw sand.

2.2. Production process of castable sand

The production process of castable sand mainly includes cold casting, warm casting, and hot casting. כַּיוֹם, the production of castable sand almost all adopts the hot casting method. The hot casting process is to heat the raw sand to a certain temperature, then mix and stir with resin, urotropine aqueous solution, and calcium stearate, בהתאמה, and then cool, crush, and sieve. Due to differences in the formula, the mixing process is also different. כַּיוֹם, there are many types of castable sand production lines in China, with about 2000 – 2300 semi-automatic lines using manual feeding and about 50 fully automatic lines using computer control, which have effectively improved production efficiency and product stability. לְדוּגמָה, the automated visual production line of the casting company, its feeding time is controlled precisely to 0.1 שניות, the heating temperature is controlled precisely אֶל 1/10 מעלות צלזיוס, and it can observe the mixing state of the sand at any time through video, with a production efficiency of 6 tons per hour.

3. Main product types of castable sand

3.1 Ordinary castable sand Common coated sand, also known as traditional coated sand, is usually composed of quartz sand, thermoplastic phenolic resin, urotropine, and calcium stearate. It does not contain any additives. The resin content is usually relatively high under certain strength requirements, and it does not possess the characteristics of high temperature resistance, low expansion, and low gas generation. It is suitable for the production of castings with low requirements.

3.2 High-strength Low-gas Release Coated Sand

מאפיינים: חוזק גבוה, low expansion, low gas generation, slow gas generation, oxidation resistance. מָבוֹא: High-strength low-gas release coated sand is an updated product of common coated sand. By adding relevant characteristics, “תוספים,” and adopting new formulation techniques, the resin dosage is significantly reduced. Its strength is more than 30% higher than that of common coated sand; the gas generation is significantly reduced, and the gas generation speed can be slowed down, which can better meet the needs of casting production. This type of coated sand is mainly suitable for the production of cast iron parts, medium and small-sized cast steel, and alloy cast steel parts. כַּיוֹם, this type of coated sand has three series: GD-1 high-strength low-gas release coated sand; GD-2 high-strength low-expansion and low-gas release coated sand; GD-3 high-strength low-expansion and low-gas release oxidation-resistant coated sand.

3.3 High-temperature-resistant (Class) חול מצופה (ND Type)

מאפיינים: High temperature resistance, חוזק גבוה, low expansion, low gas generation, slow gas generation, easy disintegration, oxidation resistance. מָבוֹא: High-temperature-resistant coated sand is a new type of coated sand with excellent high-temperature performance (high strength at high temperatures, long heat resistance time, small thermal expansion, low gas generation) and comprehensive casting performance. This type of coated sand is particularly suitable for the production of complex thin-walled precision cast iron parts (such as automotive engine blocks, cylinder heads, וכו') and high-quality cast steel parts (such as container corners, train brake buffers, middle shell parts, וכו'), which can effectively eliminate casting defects such as sticking, דֵפוֹרמַצִיָה, פיצוח תרמי, and gas pores. כַּיוֹם, this coated sand has four series: VND-1 high-temperature-resistant coated sand; ND-2 high-temperature-resistant low-expansion and low-gas release coated sand; ND-3 high-temperature-resistant low-expansion and low-gas release oxidation-resistant coated sand; ND-4 high-temperature-resistant high-strength low-expansion and low-gas release coated sand.

3.4 Easily Disintegrating Coated Sand

It has good strength and excellent low-temperature disintegration performance, suitable for the production of castings.

3.5 Other Special Requirements Coated Sand

To meet the needs of different products, a series of special coated sands have been developed, such as centrifugal casting coated sand, rapid cooling coated sand,wet-coated sand, anti-sticking sand,anti-pulse lines,anti-peeling coated sand, etc.　

סַפָּק

Luoyang Fonyo Heavy Industries Co., בע"מ,נוסדה בשנת 1998, היא יצרנית בחלקי יציקת רכבת. המפעל שלנו משתרע על שטח של 72,600㎡, עם יותר מ 300 עובדים, 32 טכנאים, לְרַבּוֹת 5 מהנדסים בכירים, 11 עוזרי מהנדסים, ו 16 טכנאים. כושר הייצור שלנו הוא 30,000 טונות בשנה. כַּיוֹם, אנחנו מייצרים בעיקר ליהוק, עיבוד שבבי, והרכבה לקטר, קְרוֹנוֹעַ, רכבות מהירות, ציוד כרייה,כוח רוח,וכו.